Metco 1220B is similar to Stellite 6 that has a finer than Metco 1220A. Deposits applied using laser cladding or PTA resist seizing, galling and cavitation over a wide temperature range, and combat adhesive, abrasive or erosive wear combined with corrosion at relatively high temperatures. They resist oxidation at temperatures up to 1000 °C (1800 °F) and resist oxidizing acids depending on the acid concentration and temperature. Self-mating surfaces have a low friction coefficient (≈ 0.12).
Characteristics
Material type | Welding/Cladding Powder |
---|---|
Product form | Powder |
Material safety datasheet number | 50-2247 |
Predesessor material |
MetcoClad 6 |
Achieved surface function primary |
Abrasion Protection Cavitation Protection Dimensional Restoration Erosion Protection in Gas Flow Erosion Protection in Liquid Flow Fretting Wear Protection Galling Resistance Sliding Wear Protection |
Suitable for service environmen |
Acidic Liquid, Not Specified Metal Melt Seawater/Brackish Water Saline Atmosphere |
Liquidus temp. | 1357 |
Solidus temp. | 1260 |
Base composition | Cobalt |
Nominal chemistry | Co 28.5Cr 4.5W 3Fe 1.6Si 1.1C |
Max. service temp. | 1000 |
Recomm metco spray gun |
3MB F4MB-XL F4MB90-XL SinplexPro |
Recommended process technology |
Brazing High-Speed Laser Cladding |
Datasheet number | DSM-0218 |